Analiza stopiwa
Mn | |||||||
Mn | Mo | C | Si | FN WRC-92 | Ni | N | Cr |
1.7 % | – | – | – | – | – | – | – |
Mo | |||||||
Mn | Mo | C | Si | FN WRC-92 | Ni | N | Cr |
– | 2.6 % | – | – | – | – | – | – |
C | |||||||
Mn | Mo | C | Si | FN WRC-92 | Ni | N | Cr |
– | – | 0.01 % | – | – | – | – | – |
Si | |||||||
Mn | Mo | C | Si | FN WRC-92 | Ni | N | Cr |
– | – | – | 0.4 % | – | – | – | – |
FN WRC-92 | |||||||
Mn | Mo | C | Si | FN WRC-92 | Ni | N | Cr |
– | – | – | – | 7 % | – | – | – |
Ni | |||||||
Mn | Mo | C | Si | FN WRC-92 | Ni | N | Cr |
– | – | – | – | – | 12.0 % | – | – |
Cr | |||||||
Mn | Mo | C | Si | FN WRC-92 | Ni | N | Cr |
– | – | – | – | – | – | – | 18.2 % |
Dopuszczenia: | CE, EN 13479, DB, 52.039.16, NAKS/HAKC, 3.2-4.0 mm, CZ, VdTÜV, 12101 |
Klasyfikacje: | S 19 12 3 L, EN ISO 14343-A, Wire Electrode, ER316L, SFA/AWS A5.9, Wire Electrode |
Rodzaj stopu: | Austenitic (with approx. 10 % ferrite) 19% Cr – 12% Ni – 3% Mo – Low C |